Build Your Online Product Catalogs?
| Product Name: |
square bar
|
| Supply Ability: |
2400 Ton/Tons |
| Related proudcts |
|
| Specifications |
Precisely-forged square bar 20mm -150mm Hot-rolled square bar |
| Price Term: |
FOB |
| Port of loading: |
ningbo or shanghai |
| Minimum Order |
2 Ton/Tons |
| Unit Price: |
|
|
square bar
Specification:
Precisely-forged square bar 20mm -150mm
Hot-rolled square bar 9.5mm*9.5mm---25.5mm*25.5mm
Application: Be used for making Hss Squrare Tool Bits, broch
Delivery Condition: Annealed, After Heat-Treatment, Finished goods
Package: Suitable for export
The ***ailed material we could offer:
1. 4Cr5MoSiV1 (GB) it is similar to H13 (ASTM), 1.2344(DIN), SKD61(JIS)
Chemical Composition: C 0.39, Si 1.10, Mn 0.30, P¡Ü0.028, S¡Ü0.020, Cr 5.10, W ¡Ü0.30,
Mo 1.35, V 0.90
Annealed Hardness: HB¡Ü235
Heat treatment temp: Hardening 1020 Temperings 530-560
Secondary 54-57HRC
Application: For making Aluminum pressing mold, extrusive mold and plastic mold
2. 4Cr5MoSiV (GB), it is similar to H11 (ASTM), 1.2343(DIN), SKD62 (JIS)
3. 3Cr2MoW8V (GB), it is similar to H21 (ASTM), 1.2581 (DIN), SKD5 (JIS)
4. W6Mo5Cr4V2 (GB), it is similar to M2( ASTM), S6-5-2(DIN), SKH51(JIS)
Chemical Composition: C 0.85, Si 0.38, Mn 0.35, P¡Ü0.030, S¡Ü0.030, Cr 4.10, W 6.00, Mo 4.80 V 1.85
Annealed Hardness: HB¡Ü255
Heat treatment temp: Hardening 1210-1230 Temperings 550
Secondary 63-65 HRC
Application: Be used widely in making all kinds of knives and durable cold working molds
5. 7Cr7Mo2V2Si (GB)
Chemical Composition: C 0.74, Si 1.10, Mn 0.45, P¡Ü0.030, S¡Ü0.030, Cr 7.10, W ¡Ü0.50,
Mo 2.10, V 1.80
Annealed Hardness: HB¡Ü255
Heat treatment temp: Hardening 1100-1150 Temperings 530
Secondary 61-63 HRC
Application: Steel for pressing mold, extrusive mold and tensile mold
|
| Company: |
zhejiang guoli tools co.,ltd
|
| Contact: |
Ms. lv jing |
| Address: |
jinyun conty hu town xinggong roas No.159 |
| Postcode: |
310404 |
| Tel: |
86 578 3156703 |
| Fax: |
86 578 3156701 |
| E-mail: |
|
|
|
|
Home